1022 steel low carbon steel wire

ASTM 1022/JIS SWRCH22K/DIN C22E(1.1151)

 

   High low carbon carburizing steel, manganese high because the strength. Plastic. Machinability and hardenability 

are slightly higher than the 15 steel, carburizing and quenching soft spot should be formed on the surface of small, 

carburizing. Carbonitriding, are wear resistant and core toughness good comprehensive performance. Hot rolling and 

normalizing good toughness. Suitable for gear, crank shaft, bracket, hinge, screw, nut, riveting and welding pieces of 

the structure, manufacturing tank etc.. Cold regions of farm implements, such as milk tank etc..

 

Product Basic Information:

 

Material		ASTM 1022
Chemical Composition		Mechanical Properties(In Quenched & Tempered State)
C	0.17-0.24	Tensile strength(MPA)	≥450
Si	0.17-0.37	Yield strength (MPA)	≥275
Mn	0.70-1.00	Elongation(δ5/%)	≥24
Cu	≤0.25	Reduction in Area (ψ/%)	≥50
Ti	-	Impact  (J)	-
P	≤0.035	Hardness	≤197HB
S	≤0.035
Cr	≤0.25
Ni	≤0.25
V	-