Oxidized bare Al aluminium wire rod for electric purpose A8

Oxidized bare Al aluminium wire rod for electric purpose A8

Specifications

It is mainly used for drawing the core of wires and cables

The surface of the rod is clean, smooth and seamless.

Coil weight: large coil≤1000kg, small coil: 300--1000kg

Aluminum Rod was produced and provided by consulting and following the American standard ASTM B233 and Germany standard EN17152

1.Producing and providing the products according to Chinese standard GB/T3954-2001, and consulting and following the American standard ASTM B233:1997, and Germany DIN standard EN 17152:1997

 

2.The Type,Condition and Range

Type	Condition	Range(mm)
A	o	Φ9-20
A2,A4,A6,A8	H/R

  aluminium rod

 

3.The Mechanics and Electric Function

Type	Tensile Strength (M pa)	Percentage Elongation (%≥)	Resistivity at 20°c (nΩ.m≤)
A	60-80	25	27.55
A2	80-100	12	27.85
A4	95-115	10	28.01
A6	110-130	8	28.01
A8	120-150	6	28.01

 

4.The Component of Material

Name of Element	Si	Fe	Cu	V+Ti+Mn+Cr	Other	Al
Percentage %	≤0.11	0.25	0.01	0.02	0.03	≥ 99.61

 

5.Standard specification for Aluminum 1350 Drawing Stock for Electrical Purposes

 

TABLE 1- Tensile Property Limits

Temper	Tensile Strength
	Ks j	M pa
1350-O	8.5-14.0	59-97
1350-H12 and-H22	12.0-17.0	83-117
1350-H14 and-H24	15.0-20.0	103-138
1350-H16 and-H26	17.0-22.0	117-152

  aluminium rod

 

TABLE 2- Electrical Resistivity Limits

Temper	Resistivity	Equivalent Volume Conductivity,%
	Max.Ω.mm2/m	IACS Min.
1350-O	0.027899	61.8
1350-H12 and-H22	0.028035	61.5
1350-H14 and-H24	0.028080	61.4
1350-H16 and-H26	0.028126	61.3